XANTAR® G8F 23 UR
| Category: | PC , Polycarbonate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | XANTAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U5Xucv_XANTAR-G8F-23-UR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% Glass Reinforced, Flame Retardant, UV Stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 3.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.30 | % | |
| Flow | 0.10 | % | |
| Water Absorption (Saturation, 23°C) | 0.23 | % | ISO 62 |
| Limiting Viscosity Number | 48.0 | cm³/g | ISO 1628-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 93 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 135 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2 |
| Flexural Modulus | 8500 | MPa | ISO 178 |
| Flexural Stress | 160 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 10 | kJ/m² | ISO 180/4A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 145 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 153 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE - Flow | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | UL 746 | ||
| 1.50 mm | 130 | °C | |
| 3.00 mm | 130 | °C | |
| RTI Imp | UL 746 | ||
| 1.50 mm | 125 | °C | |
| 3.00 mm | 130 | °C | |
| RTI Str | UL 746 | ||
| 1.50 mm | 125 | °C | |
| 3.00 mm | 130 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 29 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.40 | ||
| 1 MHz | 3.40 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 9.0E-4 | ||
| 1 MHz | 9.0E-3 | ||
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 850 | °C | |
| 3.00 mm | 875 | °C | |
| Oxygen Index | 37 | % | ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOPAS® 8007F-500 | Polyplastics Co., Ltd. | COC | TOPAS® |
| Celcon® M270™ | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| INTENE® 60 AF | Versalis S.p.A. | PBR, Low Cis | INTENE® |
| LNP™ STAT-KON™ Noryl_NC2525 compound | SABIC Innovative Plastics Europe | PPE+PS | LNP™ STAT-KON™ |
| LNP™ STAT-KON™ OE002 compound | SABIC Innovative Plastics | PPS, Linear | LNP™ STAT-KON™ |