Matrixx CPP3B30
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | The Matrixx Group, Inc. |
| Trademark: | Matrixx |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U5HoWQ_Matrixx-CPP3B30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Matrixx CPP3B30 is a polypropylene copolymer (PP Copoly) material, which contains 30% calcium carbonate filler. This product is available in North America and is processed by injection molding. The main features of the Matrixx CPP3B30 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 1.0 - 1.4 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 19.3 | MPa | ASTM D638 |
| Flexural Modulus - Tangent | 1480 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 120 | J/m | ASTM D256 |
| Dart Drop Impact | 18.1 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| RTI | 65.6 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 104 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 188 - 232 | °C | |
| Middle Temperature | 188 - 232 | °C | |
| Front Temperature | 188 - 232 | °C | |
| Processing (Melt) Temp | 199 - 232 | °C | |
| Mold Temperature | 21.1 - 48.9 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.138 - 2.07 | MPa | |
| Cushion | 6.35 - 12.7 | mm |
| Injection instructions |
|---|
| Drying not normally requiredInjection Booster Pressure: Maximum without flash, 60% of machine maximum, targetScrew Speed: Slow to Medium |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® F34 | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| TAISOX 3210 | Formosa Plastics Corporation | LLDPE | TAISOX |
| TARFLON™ NEO GGK1740 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| ALFATER XL® A90I 4FC0000 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |
| Dynaflex™ G2712-1000-02 | PolyOne Corporation | TPE | Dynaflex™ |