Nypol® PA A3 G30 HL CNZA178 NR466 MSP
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U5G4MR_Nypol-PA-A3-G30-HL-CNZA178-NR466-MSP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 in gray color reinforced with 30% of fiberglass, lubricated and improved flow. Good set of thermal and mechanical properties. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 to 1.38 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage (3.20 mm) | 0.30 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 6.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.9 | -- | % | |
| Ash Content | 28.0 to 32.0 | -- | ISO 1172 | |
| Relative Viscosity - Formic Acid | 46.0 to 52.0 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9700 | 7000 | MPa | ISO 527-2 |
| Tensile Stress | 200 | 135 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.2 | 5.0 | % | ISO 527-2 |
| Flexural Modulus | 12200 | 6500 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact Strength | ||||
| 23°C | -- | 14 | kJ/m² | ISO 180/1A |
| 23°C | 11 | -- | kJ/m² | ISO 180/2A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | -- | 70 | kJ/m² | |
| 23°C | > 70 | > 70 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 260 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 250 to 265 | -- | °C | ISO 3146 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 270 to 285 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 80S7451 | The Matrixx Group, Inc. | PET | Matrixx |
| Nivionplast® B R50G NERO | SO.F.TER. SPA | Nylon 6 | Nivionplast® B |
| ALCOM® PC 740/4 UV OR1075-05LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| Felix Compounds Mica | Felix Compounds | PP+PE | Felix Compounds |
| Dynacom CT-118 | Dynachem Co. Ltd. | PP Copolymer | Dynacom |