Modified Plastics MN 6/6-FG 20
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Modified Plastics, Inc. |
| Trademark: | Modified Plastics |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U4gckM_Modified-Plastics-MN-6-6-FG-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Modified Plastics MN 6/6-FG 20 is a Polyamide 66 (Nylon 66) product filled with 20% glass fiber. It can be processed by injection molding and is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.70 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 1.1 | % | |
| Saturation | 5.3 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 125 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 3.5 | % | ASTM D638 |
| Flexural Modulus | 5520 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 193 | MPa | ASTM D790 |
| Compressive Strength | 154 | MPa | ASTM D695 |
| Shear Strength | 68.9 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm) | 59 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 6.35 mm) | 370 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 260 | °C | |
| 1.8 MPa, Unannealed | 252 | °C | |
| CLTE - Flow | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 100 Hz | 4.30 | ||
| 1 kHz | 2.10 | ||
| 1 MHz | 3.80 | ||
| Dissipation Factor (1 MHz) | 0.020 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Processing (Melt) Temp | 271 to 299 | °C | |
| Mold Temperature | 93.3 to 107 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecnoflon® N 215 | Solvay Specialty Polymers | Fluorelastomer | Tecnoflon® |
| Ferro PP NPP00GT01NA | Ferro Corporation | PP, Unspecified | Ferro PP |
| HIDEN® P301E | YUHWA Korea Petrochemical Ind. Co., Ltd. | HDPE | HIDEN® |
| Pearlthane® ECO D12T80 | Lubrizol Advanced Materials, Inc. | TPU, Unspecified | Pearlthane® ECO |
| PENTAMID L GV30 H schwarz | PENTAC Polymer GmbH | Nylon 12 | PENTAMID L |