Daelim Po1y® LH-148
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | DAELIM INDUSTRIAL CO., LTD. |
| Trademark: | Daelim Po1y® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U3oF2N_Daelim-Po1y-LH-148.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Daelim Po1y®LH-148 is a high density polyethylene product,. It can be processed by filament extrusion and is available in the Asia Pacific region. Typical application areas are: slings/ropes. The main characteristics are: good processing performance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.943 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.2 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 26.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 900 | % | ASTM D638 |
| Flexural Modulus | 981 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -118 | °C | ASTM D746 |
| Additional Information |
|---|
| Ultimate Elongation, ASTM D-638, Type VI Spec, 50 mm/min: >900%Brittle Temperature, ASTM D-746: <-118°C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 250 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SWANCOR Epoxy 908 | SWANCOR IND. CO., LTD. | Epoxy | SWANCOR Epoxy |
| UBE Nylon 5034 UC2 | UBE Engineering Plastics, S.A. | Nylon 66/6 | UBE Nylon |
| TECHLEN SD810 | DAEHA Co., LTD | PP, Unspecified | TECHLEN |
| Braskem PP TI6120AN | Braskem America Inc. | PP Impact Copolymer | Braskem PP |
| Delas 175 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PVC+NBR | Delas |