Duroloy® AS-81
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Unigel Plásticos |
| Trademark: | Duroloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U3Zhpn_Duroloy-AS-81.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Medium flow rate and high impact grade. For injection molding. Main applications: automotive and electrical-electronic. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 12 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.55 to 0.75 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 53.0 | MPa | |
| Break | 53.0 | MPa | |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield | 5.0 | % | |
| Break | 130 | % | |
| Flexural Modulus | 2300 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 340 | J/m | |
| 23°C, 3.20 mm | 600 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 127 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 109 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 109 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 133 | °C | ASTM D1525, ISO 306/B50 2 1 |
| -- | 135 | °C | ASTM D1525, ISO 306/B120 3 2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 250 | °C | |
| Middle Temperature | 260 | °C | |
| Front Temperature | 270 | °C | |
| Nozzle Temperature | 260 | °C | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| 2 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 4DUR® 9K23100 H | 4Plas | PBT | 4DUR® |
| ICORENE® N4425 | ICO Polymers EMEA, A Division of A. Schulman | PP Homopolymer | ICORENE® |
| IDI BMC B10 (Glass Content 15%) | IDI Composites International | TS, Unspecified | IDI BMC |
| Sylvin 6920X08 Red 6306 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Durethan® B 35 FKA 000000 | LANXESS GmbH | Nylon 6 | Durethan® |