| Category: | EBA , Ethylene Butyl Acrylate Copolymer |
| Manufacturer: | Arkema |
| Trademark: | Lotryl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U38E6d_Lotryl-28BA175.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LOTRYL® 28BA175 is a random copolymer of Ethylene and Butyl Acrylate produced by high-pressure radicalar polymerization process. Applications Due to the high butyl acrylate content, LOTRYL® 28BA175 can be used for applications where flexibility and polarity are required. Combined with a high fluidity, LOTRYL® 28BA175 is particularly recommended for the formulation of hot melt adhesives. It can also be used as processing-aid in highly filled compounds. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 150 to 200 | g/10 min | ASTM D1238, ISO 1133 |
| n-Butyl Acrylate Content | 26.0 to 30.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, Compression Molded) | 80 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 3.00 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, Compression Molded) | 300 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus (Compression Molded) | 23.0 | MPa | ASTM D790, ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 40.0 | °C | ISO 306/A, ASTM D1525 1 |
| Melting Temperature | 75.0 | °C | ISO 11357-3 |
| Ring and Ball Softening Point | 94 | °C | ASTM E28 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 to 170 | °C | |
| Cylinder Zone 2 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 170 | °C | |
| Cylinder Zone 4 Temp. | 170 | °C | |
| Die Temperature | 170 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vamac® G | DuPont Performance Elastomers | AEM | Vamac® |
| NORYL™ PN275F resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| Anjacom® 050/7020 | Almaak International GmbH | PC+ABS | Anjacom® |
| Colorite Rigid PVC 1118G-WHITE 532 | Colorite Polymers | PVC, Rigid | Colorite Rigid PVC |
| ProPolymers PAA 4000 | ProPolymers Inc. | Nylon Copolymer | ProPolymers |