Kynar Flex® 3120-10
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | Arkema |
| Trademark: | Kynar Flex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U2OhYi_Kynar-Flex-3120-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KYNAR FLEX® 3120-10 is a pelletized, semi-crystalline VF2 based copolymer. KYNAR FLEX® 3120-10 can be extruded or injection molded to make final products with a 150°C rating. ADDITIONAL CHARACTERISTICS: Excellent thermal stability Excellent abrasion resistance Impervious to UV degradation |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.77 to 1.79 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 65 to 70 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 24.1 to 34.5 | MPa | |
| Break, 23°C | 34.5 to 48.3 | MPa | |
| Tensile Elongation (Break, 23°C) | 300 to 550 | % | ASTM D638 |
| Flexural Modulus (23°C) | 621 to 827 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 20.7 to 34.5 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 31.0 to 41.4 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 161 to 168 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 1(20°C) | 2.0E+14 | ohms·cm | ASTM D257 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (232°C, 100 sec^-1) | 400 to 1200 | Pa·s | ASTM D3835 |
| Note Message | |
|---|---|
| 1 . | 65% R.H. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E585PUOO | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| ResMart ABS VH-0800 Black | ResMart | ABS | ResMart |
| Ultradur® B 4300 G2 FC | BASF Corporation | PBT | Ultradur® |
| ARMAMID® PA NE 30.1 | Poly Plastic | Nylon 6 | ARMAMID® |
| LNP™ LUBRICOMP™ DBL32 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |