NYCOA Polyamide 2090 HS
| Category: | Nylon+TPE , Polyamide + TPE |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U29sqY_NYCOA-Polyamide-2090-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 2090 HS is a medium viscosity Nylon copolymer TPE particularly suitable for extrusion applications. This material offers an outstanding balance of toughness, flexibility, and strength, with improved flame retardancy. The high thermal and chemical resistance, inherent to Nylon 6, is retained. NYCOA 2090 HS provides high melt viscosity and melt strength and hence outstanding processability for tubing, profile, sheet, and monofilament. This product is available with custom additive packages: UV stabilizer, and custom colors. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.2 | % | ASTM D955 |
| Transverse flow | 1.4 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.7 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 49.6 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 400 | % | ASTM D638 |
| Flexural Modulus 3 | 586 | MPa | ASTM D790 |
| Flexural Strength 4 | 23.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 204 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 216 - 227 | °C | |
| Middle Temperature | 221 - 238 | °C | |
| Front Temperature | 232 - 249 | °C | |
| Nozzle Temperature | 243 - 260 | °C | |
| Processing (Melt) Temp | 243 - 254 | °C | |
| Mold Temperature | 21.1 - 48.9 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.138 - 0.345 | MPa | |
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 18.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Razalen® P111 | Razin™ Engineering Plastics | PP Impact Copolymer | Razalen® |
| RTP 100 TFE 10 | RTP Company | PP, Unspecified | RTP |
| TRIEL® 5451GP | Samyang Corporation | TPEE | TRIEL® |
| Zetpol® 0020 | Zeon Corporation | NBR | Zetpol® |
| LUBEMID B27 GF25 NATURAL | LUBEN PLAST srl | Nylon 6 | LUBEMID |