| LLBF-223G is a certified prime resin Butene-comonomer, designed for production of high drawdown, high output general purpose packaging Blown films. LLBF-223G features a combination of excellent processability with good film strength as well as wide heat sealing temperature range. LLBF-223G major applications include garment bags, produce bags and liners. Maximum recommended film drawdown is 0.5 mil. LLBF-223G contains high slip and very high antiblock. LLBF-223G complies with FDA regulation 21CFR 177.1520 (c) 3.1(a) and most international regulations concerning the use of Polyethylene in contact with food articles. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm | 179 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm | 193 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 8.27 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 8.27 | MPa | ASTM D882 |
| MD : Break, 25 µm | 36.5 | MPa | ASTM D882 |
| TD : Break, 25 µm | 26.2 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 650 | % | ASTM D882 |
| TD : Break, 25 µm | 780 | % | ASTM D882 |
| Dart Drop Impact 1(25 µm) | 70 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 120 | g | ASTM D1922 |
| TD : 25 µm | 340 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.4 µm, Blown Film) | 22 | ASTM D2457 | |
| Haze (25.4 µm, Blown Film) | 29 | % | ASTM D1003 |
| Additional Information |
|---|
| Film Specimen: 1.0 mils (25 µm) film, melt temperature 395-430°F (200-220°C), blow-up-ratio 2.5 :1 |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2100 TFE 15 | RTP Company | PEI | RTP |
| RTP 6011-75A | RTP Company | TPE | RTP |
| Karina OCHER PVC COMPOUND 810-37/3-CRB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lutene® XL2808BK TR | LG Chem Ltd. | PE, Unspecified | Lutene® |
| Sylvin 8707-84 Grey 9533 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |