Elastollan® 1185 A 15 000
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | BASF Polyurethanes GmbH |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U0yQXM_Elastollan1185A15000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermoplastic Polyether-Polyurethane with outstanding hydrolysis resistance, low temperature flexibility and high resistance to micro-organisms. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183/A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 3 sec) | 87 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 25.0 | mm³ | ISO 4649-A |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | DIN 53504-S2 | ||
| 20% strain | 3.00 | MPa | DIN 53504-S2 |
| 100% strain | 7.00 | MPa | DIN 53504-S2 |
| 300% strain | 12.0 | MPa | DIN 53504-S2 |
| Tensile Stress | DIN 53504-S2 | ||
| Yield | 45.0 | MPa | DIN 53504-S2 |
| Yield 1 | 32.0 | MPa | DIN 53504-S2 |
| Tensile Elongation (Break) | 600 | % | DIN 53504-S2 |
| Tear Strength 2 | 70 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 25 | % | ISO 815 |
| 70°C, 24 hr | 45 | % | ISO 815 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | No Break | ISO 179 | |
| 23°C | No Break | ISO 179 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 - 90 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40 | °C | |
| Rear Temperature | 205 - 215 | °C | |
| Middle Temperature | 210 - 225 | °C | |
| Front Temperature | 215 - 225 | °C | |
| Nozzle Temperature | 220 - 230 | °C | |
| Processing (Melt) Temp | 215 - 225 | °C | |
| Mold Temperature | 20 - 40 | °C | |
| Injection Rate | Slow | ||
| Back Pressure | 5.00 - 15.0 | MPa |
| Note Message | |
|---|---|
| 1 . | after storage in water at 80°C for 42 days |
| 2 . | Method B, right-angle specimen (cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Biogreen 650 | Primex Plastics Corporation | Biodeg Polymers | Prime Biogreen |
| Sinvicomp SBB3704UV | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Sinpolene MBB1232 | Teknor Apex Asia Pacific PTE. LTD. | PE, Unspecified | Sinpolene |
| Braskem PE HS5502 | Braskem | HDPE | Braskem PE |
| Karina WHITE COLOR CONCENTRATE -E 10/ 31-RG-GE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |