Boltaron 9915 FSTH
| Category: | PMMA+PVC , Acrylic (PMMA) + PVC |
| Manufacturer: | Boltaron Performance Products |
| Trademark: | Boltaron |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U0wbAk_Boltaron-9915-FSTH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fully Compliant Aircraft Grade Thermoplastic Sheet - Airbus and Boeing compliance never looked so good With Boltaron 9915 FSTH, designers now have the flexibility to produce visually stunning aircraft interior components, while also meeting all Boeing and Airbus requirements for flammability, smoke, toxicity, and heat release. Constructed with Lexan XHR6000 high performance thermoplastic sheet manufactured by SABIC Innovative Plastics, Boltaron 9915 FSTH is a proprietary composite offered in a combination of decorative designs, colors, and textures unavailable from any other film and sheet supplier. Offered in decorative effects such as wood-grain, pearlescent, and carbon-fiber, Boltaron 9915 FSTH gives designers the flexibility to produce eye-popping 2-and 3- dimensional seating components, shrouds, and panels. In addition, Boltaron 9915 FSTH is the only fully compliant aircraft grade thermoplastic sheet with a low- gloss surface after thermoforming, allowing for consistent part-to-part appearance. With an unparalleled combination of physical properties and design flexibility, compliance with toxicity standards never looked better. Meets toxicity requirements per ABD0031, BSS7239, and D6-5137 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (Thermoformed) | 0.50 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 73.1 | MPa | ASTM D638 |
| Flexural Modulus | 2500 | MPa | ASTM D790 |
| Flexural Strength | 115 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 190 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 121 | °C | ASTM D648 |
| CLTE - Flow (-40 to 40°C) | 5.8E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability | |||
| -- | Pass | FAR 25.853(d) | |
| 12 sec | Pass | FAR 25.853 | |
| 60 sec | Pass | FAR 25.853 | |
| Heat Release 1 | FAR 25.853 | ||
| 2 min | < 65 | kW·min/m² | |
| Peak | < 65 | kW/m² | |
| Smoke Toxicity 2 | Pass |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Ds | ASTM F814 | ||
| 1.5 min | < 100 | ||
| 4 min | < 200 |
| Note Message | |
|---|---|
| 1 . | A1 F, Part IV |
| 2 . | ABD-0031, BSS-7239, D6-51377 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WINTEC™ WFW4F | Japan Polychem Corporation | PP Random Copolymer | WINTEC™ |
| 3M™ Dyneon™ Fluoroplastic THV 815GZ | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroplastic |
| Clariant Nylon 6/6 PA-111G33C | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Extir® LN 2000 | Versalis S.p.A. | PS (EPS) | Extir® |
| LNP™ LUBRICOMP™ IFL36R compound | SABIC Innovative Plastics Europe | Nylon 612 | LNP™ LUBRICOMP™ |