Moplen HP2973
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U0TRLx_MoplenHP2973.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Moplen HP2973 is a modified polypropylene homopolymer designed for the production of BOPP films at very high speed. BOPP films produced with HP2973 feature good mechanical properties, excellent barrier against moisture, odours, oxygen, and good transparency and gloss. Coextruded films made of Moplen HP2973 are widely used in the food packaging industry. Moplen HP2973 is formulated with slip agent and antistatic. For regulatory information please refer to Moplen HP2973 Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 70 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1450 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 34.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 10 | % | ISO 527-2/50 |
| Fracture | 410 | % | ISO 527-2/50 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Tangent 1(20 µm) | 2400 | MPa | MA 18068 |
| Tensile Stress 2(Break, 20 µm) | 116 | MPa | MA 18068 |
| Tensile Elongation 3(Break, 20 µm) | 29 | % | MA 18068 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 88.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 152 | °C | ISO 306/A50 |
| Note Message | |
|---|---|
| 1 . | 5 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6000 GS 25 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Varcum 29116 | Durez Corporation | Phenolic | Varcum |
| Epiall® 1908M-1 | Sumitomo Bakelite North America, Inc. | Epoxy | Epiall® |
| POCAN® B 1205 XF 000000 | LANXESS Asia/Pacific | PBT | POCAN® |
| Osterlene® PPH035LWC | Osterman & Company | PP Homopolymer | Osterlene® |