Sasol Polymers PE HF121
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Sasol Polymers |
| Trademark: | Sasol Polymers PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U0GGOG_Sasol-Polymers-PE-HF121.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Features
Applications
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| With itself-dynamic, blown film | 0.14 | ASTM D1894 | |
| With itself-static, blown film | 0.14 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 30 µm, blown film | 13.0 | MPa | ASTM D882 |
| TD : Yield, 30 µm, blown film | 11.0 | MPa | ASTM D882 |
| MD : Broken, 30 µm, blown film | 34.0 | MPa | ASTM D882 |
| TD : Broken, 30 µm, blown film | 25.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 30 µm, blown film | 530 | % | ASTM D882 |
| TD : Yield, 30 µm, blown film | 650 | % | ASTM D882 |
| Dart Drop Impact 1(30 µm, Blown Film) | 140 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 30 µm, blown film | 9.0 | g | ASTM D1922 |
| TD : 30 µm, blown film | 28 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 51 | ASTM D2457 | |
| Haze | 12 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blocking | 19 | g | ASTM D3354 |
| The above values were calculated from data for 30µm film produced on a 75mm Barmag extruder with 190°C melt temperature using a 2:1 blow ratio and a die gap of 3.0mm. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 180 - 190 | °C | |
| Cylinder Zone 1 Temp. | 190 - 200 | °C | |
| Cylinder Zone 2 Temp. | 190 - 200 | °C | |
| Cylinder Zone 3 Temp. | 190 - 200 | °C | |
| Cylinder Zone 4 Temp. | 190 - 200 | °C | |
| Melt Temperature | 190 | °C | |
| Die Temperature | 190 - 200 | °C |
| Extrusion instructions |
|---|
| Screen Pack: 20/40/20 BS meshBlow ratio: >2:1 |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 524M | Saudi Basic Industries Corporation (SABIC) | PP Homopolymer | SABIC® PP |
| Sylvin 2905-85 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Toraycon® 1164G-30 FE | Toray Resin Company | PBT | Toraycon® |
| Hylex® P1017G30HB | Ravago Manufacturing Americas, LLC | PC | Hylex® |
| Osterlene® LLDB-2-919 | Osterman & Company | LLDPE | Osterlene® |