Epocast 1614-A1
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Huntsman Advanced Materials |
| Trademark: | Epocast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TzbWW2_Epocast-1614-A1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DESCRIPTION: Epocast ® 1614-A1 epoxy structural syntactic is a low-density, frozen, one-component material for use on honeycomb composite parts requiring high compressive strength at service temperatures up to 350°F (177°C). Epocast ® 1614-A1 epoxy structural syntactic may also be used for fastener or attachment potting and panel edge reinforcing. It is qualified to BMS 5-28, Type 14, Classes 1 and 2 and other specifications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.750 | g/cm³ | ASTM D1622 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | ASTM D695 | ||
| 177°C | 48.0 | MPa | ASTM D695 |
| 121°C | 69.0 | MPa | ASTM D695 |
| 25°C | 100 | MPa | ASTM D695 |
| Flammability | Nominal Value | ||
|---|---|---|---|
| Flammability | Self Extinguishing |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Extrudability (25°C) | 800 | g/min | BMS 5-28 |
| Tensile Lap Shear - AL/AL | 6.89 | MPa | ASTM D1002 |
| Weight Gain 1 | ASTM D543 | ||
| Distilled Water : 25°C | 0.20 | % | ASTM D543 |
| Mil-H-5606 hydraulic fluid : 25°C | 0.30 | % | ASTM D543 |
| Mil-S-3136, Type III test fluid : 25°C | 0.10 | % | ASTM D543 |
| Skydol hydraulic fluid : 25°C | 0.20 | % | ASTM D543 |
| Work Life (25°C) 2 | 8.0 | hr | ASTM D1338 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shelf Life (-29°C) | 13 | wk |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CURE SCHEDULE: Heat the material from room temperature at the rate of 5-7°F (3-4°C) per minute, plus 1 hour at 350°F (177°C) or 90 minutes at 250°F (121°C). Cure temperature refers to temperature of material as determined by thermocouple. (Slow heat rise at 5-7°F (3-4°C) per minute is preferred to reduce shrinkage and minimize out-gassing during cure). |
| Note Message | |
|---|---|
| 1 . | 24 hrs |
| 2 . | after thaw |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V929_02 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Badaflex® TPE-S 45A 1000LD | Bada AG | TPE | Badaflex® |
| Celazole® (T Series) TL-60 | PBI Performance Products, Inc. | PBI | Celazole® (T Series) |
| TECHNYL® B 216 BLACK 3N | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® |
| Kepamid® 1315GFH | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |