Durethan® AM 430 H2.0 901510
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TyoDDz_Durethan-AM-430-H2-0-901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66, 30% mineral, injection molding, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.39 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | |||
| Across Flow : 290°C, 2.00 mm 1 | 1.2 | -- | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.30 | -- | % | |
| Flow : 290°C, 2.00 mm 3 | 1.0 | -- | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.20 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 4800 | 2000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 80.0 | 40.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 4.0 | 50 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 4900 | 2100 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% Strain, 23°C | 130 | 50.0 | MPa | |
| 23°C 6 | 140 | 60.0 | MPa | |
| Flexural Strain at Flexural Strength 7(23°C) | 5.0 | 7.5 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 66, GHR, 14-050, MD30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | < 10 | < 10 | kJ/m² | |
| 23°C | < 10 | < 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 60 | -- | kJ/m² | |
| 23°C | 70 | 120 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | < 10 | < 10 | kJ/m² | |
| 23°C | < 10 | < 10 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 50 | -- | kJ/m² | |
| 23°C | 60 | 110 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 90.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 244 | -- | °C | ISO 306/B120 |
| Melting Temperature 8 | 262 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 6.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 8.0E-5 | -- | cm/cm/°C |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Westlake MDPE EB171 | Westlake Chemical Corporation | MDPE | Westlake MDPE |
| Yanshan PE 2300XM | SINOPEC Beijing Yanshan Petrochemical | HDPE | Yanshan PE |
| Nucrel® 0902HC | DuPont Packaging & Industrial Polymers | EMAA | Nucrel® |
| BCC Resins BC 8690E | BCC Products Inc. | TSU | BCC Resins |
| LNP™ LUBRICOMP™ EL003 compound | SABIC Innovative Plastics | PEI | LNP™ LUBRICOMP™ |