DOW™ LDPE 722

Category:	LDPE , Low Density Polyethylene Resin
Manufacturer:	The Dow Chemical Company
Trademark:	DOW™ LDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	TybYG1_DOW-LDPE-722.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

DOW polyethylene 722 has a wide molecular weight distribution. This homopolymer has good impact strength and crack resistance, and it also has excellent flexibility. This resin has good processing performance and wide processing range.

low density polyethylene (LDPE)

Typical applications include capping materials

Good impact strength, good environmental stress cracking resistance, good ESCR performance, and excellent flexibility

Comply with the following regulations:

Canadian Health Products and Food Agency (HPFB) requirements: no objections (with restrictions)

EU, No 10/2011

U.S. Food and Drug Administration Regulation 21 CFR 177.1520 (c) 2.2

U.S. Food and Drug Administration Drug Master File (DMF)

Please check the regulations for complete details.

General Information
Agency Ratings	DMF not rated FDA 21 CFR 177.1520(c) 2.2 HPFB (Canada) No Objection 2 Europe No 10/2011
Forms	Particle
Processing Method	Extrusion coating Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.918	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	8.0	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance ¹(50°C, 100% Igepal, F50)	< 1.00	hr	ASTM D1693

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness ²(Shore D)	43		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ³			ASTM D638
Yield	8.27	MPa	ASTM D638
Fracture	9.65	MPa	ASTM D638
Tensile Elongation ⁴			ASTM D638
Yield	4.0	%	ASTM D638
Fracture	500	%	ASTM D638
Flexural Modulus - 2% Secant ⁵	234	MPa	ASTM D790B
Coefficient of Friction	0.60		ASTM D1894

Films	Nominal Value	Unit	Test Method
Seal Initiation Temperature ⁶	105	°C	Internal method
Water Vapor Transmission Rate	0.67	g·mm/m²/atm/24 hr	ASTM F1249

Impact	Nominal Value	Unit	Test Method
Tensile Impact Strength	273	kJ/m²	ASTM D1822

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load ⁷(0.45 MPa, Unannealed)	37.2	°C	ASTM D648
Brittleness Temperature ⁸	-60.0	°C	ASTM D746
Vicat Softening Temperature	87.8	°C	ASTM D1525
Melting Temperature (DSC)	107	°C	Internal method
Peak Crystallization Temperature (DSC)	95.6	°C	Internal method

Additional Information	Nominal Value	Unit	Test Method
Melt temperature- Recommended	316 - 332	°C	Internal method

Extrusion	Nominal Value	Unit	Test Method
Neck-in (321°C, 25.4 µm)	50.8	mm	Internal method
Maximum production line speed	7.6	m/sec	Internal method
Minimum coating thickness	7.6	µm	Internal method
Minimum coating weight	7.2	g/m²	Internal method

Additional Information	Nominal Value	Unit	Test Method
Fabrication Conditions For Extrusion Coating Film: Screw Size: 3.5 in. (89 mm); 30:1 L/D Screw Type: Single Flight with Maddock Mixer Die Gap: 20 mil (0.508 mm) Melt Temperature: 625°F (329°C) Output: 250 lb/hr Screw Speed: 90 rpm

Note Message
1 .	Molding and testing according to ASTM D 4976.
2 .	Molding and testing according to ASTM D 4976.
3 .	Molding and testing according to ASTM D 4976.
4 .	Molding and testing according to ASTM D 4976.
5 .	Molding and testing according to ASTM D 4976.
6 .	Temperature at which 1 lb/in (4.4 N/25.4 mm) heat seal strength is achieved.Heat Seal Strengths, Topware HT Tester 0.5 S dwell, 40 pis bar pressure, pull speed 250 mm/sec.
7 .	Molding and testing according to ASTM D 4976.
8 .	Molding and testing according to ASTM D 4976.

Resin Grade	Manufacturer	Category	Trademark
Mirakutoran® TPU P885	Japan Mirakutoran Inc.	TPU Alloy	Mirakutoran® TPU
AT 191A	Celanese EVA Performance Polymers	LDPE	AT
GLS Acetal UN02	GLS Polymers Pvt. Ltd.	Acetal (POM) Copolymer	GLS Acetal
Hyundai EP PA66 LD130	HYUNDAI EP Co., Ltd.	Nylon 66	Hyundai EP PA66
apilon 52® FA-8505	API SpA	TPU-Polyester	apilon 52®