Prime Tuff-X 200 HG

Category:	Unspecified , Unspecified
Manufacturer:	Primex Plastics Corporation
Trademark:	Prime Tuff-X
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	TxwIMp_Prime-Tuff-X-200-HG.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Prime Tuff-X 200 HG offers the same great benefit as our Tuff-X 200 but also has a very high gloss before and after forming. Using the Gardner Gloss Meter at 60° angle gloss levels of 85 to 90 have been obtained after forming. Applications: This combination of materials is ideal for such applications as automotive, power tools, irrigation, fluid handling, lawn and garden, electronics, RV Interior and exterior parts. Processing: Prime Tuff-X 200 HG is a Semi-crystalline material that behaves differently in the thermoforming process when compared to an amorphous material like HIPS or ABS. Ideal forming conditions; mold temp. 170-190°F, Sheet temp. 320-360°F, part removal temp. 145-170°F. Aluminum temperature controlled grit blasted tools are preferred. Ceramic tools also work well if glass bead blasted. Quartz or ceramic heaters are preferred when working with Tuff-X. Calrod heaters may sometimes be used but gas fired ovens are not recommended. Finishing: Prime Tuff-X 200 HG can be fabricated by using the same method as the Prime Tuff-X 200. It may also be bonded by using certain adhesives. Prime Tuff-X 200 HG has a high gloss that can even improve in the thermoforming process if properly heated. Scratch and mar issues can be repaired on the gloss surface. Please contact your Primex Plastics representative for more information on finishing, fabricating, or the thermoforming process. Colors, Textures and Capabilities: Prime Tuff-X 200 HG is capable of accepting any color. The substrate may be color matched or a field of color. Both the cap and the substrate are capable of holding < 1.5 Delta E. Tuff-X 200 HG is offered in gauges ranging from .090 to .400 in. and widths up to 120". There are several different patterns available, however, typically this product is used when a smooth high-gloss appearance is required.

Message

Prime Tuff-X 200 HG offers the same great benefit as our Tuff-X 200 but also has a very high gloss before and after forming. Using the Gardner Gloss Meter at 60° angle gloss levels of 85 to 90 have been obtained after forming.

Applications:
This combination of materials is ideal for such applications as automotive, power tools, irrigation, fluid handling, lawn and garden, electronics, RV Interior and exterior parts.

Processing:
Prime Tuff-X 200 HG is a Semi-crystalline material that behaves differently in the thermoforming process when compared to an amorphous material like HIPS or ABS. Ideal forming conditions; mold temp. 170-190°F, Sheet temp. 320-360°F, part removal temp. 145-170°F. Aluminum temperature controlled grit blasted tools are preferred. Ceramic tools also work well if glass bead blasted. Quartz or ceramic heaters are preferred when working with Tuff-X. Calrod heaters may sometimes be used but gas fired ovens are not recommended.

Finishing:
Prime Tuff-X 200 HG can be fabricated by using the same method as the Prime Tuff-X 200. It may also be bonded by using certain adhesives. Prime Tuff-X 200 HG has a high gloss that can even improve in the thermoforming process if properly heated. Scratch and mar issues can be repaired on the gloss surface.

Please contact your Primex Plastics representative for more information on finishing, fabricating, or the thermoforming process.

Colors, Textures and Capabilities:
Prime Tuff-X 200 HG is capable of accepting any color. The substrate may be color matched or a field of color. Both the cap and the substrate are capable of holding < 1.5 Delta E. Tuff-X 200 HG is offered in gauges ranging from .090 to .400 in. and widths up to 120". There are several different patterns available, however, typically this product is used when a smooth high-gloss appearance is required.

General Information
Features	Good Chemical Resistance Good Colorability Good UV Resistance High Gloss High Heat Resistance High Impact Resistance High Tensile Strength Low Temperature Impact Resistance Semi Crystalline
Uses	Automotive Applications Electrical/Electronic Applications Lawn and Garden Equipment Power/Other Tools Sporting Goods
Appearance	Colors Available
Forms	Sheet
Processing Method	Thermoforming

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.06	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR)	1.1	g/10 min	ASTM D1238

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	67		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	20.2	MPa	ASTM D638
Flexural Modulus	1670	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	720	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	102	°C	ASTM D648
CLTE - Flow	4.9E-5	cm/cm/°C	ASTM D696

Additional Information	Nominal Value	Unit
De-mold Temperature	63 to 77	°C
Mold Temperature (other)	77 to 88	°C
Sheet Temperature	160 to 182	°C

Resin Grade	Manufacturer	Category	Trademark
Sinvicomp DBS3613	Teknor Apex Asia Pacific PTE. LTD.	PVC, Rigid	Sinvicomp
Caltex PP MT64WS	GS Caltex	PP, Unspecified	Caltex PP
Daelim Po1y® PR-770B	DAELIM INDUSTRIAL CO., LTD.	PP Homopolymer	Daelim Po1y®
Sumiliteresin® PR-217 I	SBHPP	Phenolic	Sumiliteresin®
RTP 205.3 B	RTP Company	Nylon 610	RTP