Hyosung Polyketone M330A Medium viscosity grade for injection molding (Natural color) |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (240°C/2.16 kg) | 60 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.8 to 2.0 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.50 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 58.8 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | > 250 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1370 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 58.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 98.1 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 210 | °C | |
| 1.8 MPa, Unannealed | 105 | °C | |
| Melting Temperature | 220 | °C | ASTM D1525 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Melos™ FM 303 | Melos GmbH | IIR | Melos™ |
| NILENE® E10 K30T | Taro Plast S.p.A. | PP Copolymer | NILENE® |
| Evolue™-H SP50800P | Prime Polymer Co., Ltd. | HDPE | Evolue™-H |
| Hostacom SZ021-2 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Elastofoam® 38100R / 3120T | BASF Corporation | PUR, Unspecified | Elastofoam® |