TARFLON™ SK2708
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Idemitsu Kosan Co., Ltd. |
| Trademark: | TARFLON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TvUmvd_TARFLON-SK2708.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High flow, High impact |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 23.0 | cm³/10min | ISO 1133 |
| Spiral Flow | 45.0 | cm | Internal Method |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 2.00 mm | 0.30 to 0.40 | % | |
| Flow : 2.00 mm | 0.30 to 0.40 | % | |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 64.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 60 | % | ISO 527-2 |
| Flexural Modulus | 2900 | MPa | ISO 178 |
| Flexural Stress | 96.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 88.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 78.0 | °C | ISO 75-2/A |
| CLTE - Flow | 6.5E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 85.0 | °C | UL 746 |
| RTI Imp | 85.0 | °C | UL 746 |
| RTI Str | 85.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.900 mm | V-1 | ||
| 1.50 mm | V-0 | ||
| 1.20 mm | 5VB |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| ISO Shortname | >PC+ABS-FR(40)< |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 5.0 to 8.0 | hr | |
| Rear Temperature | 240 to 270 | °C | |
| Middle Temperature | 240 to 270 | °C | |
| Front Temperature | 240 to 270 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 24h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pyramid™ PEEK KD2000-R02 | Polymics, Ltd. | PEEK | Pyramid™ PEEK |
| Niche PPHM6BK | Niche Polymer, LLC | PP Homopolymer | Niche |
| Chemlon® A40 | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Comai 733-2 AB | Comai Ltda | LLDPE | Comai |
| ESTOPLAST SR 1500GY06 | Ester Industries Ltd. | ABS | ESTOPLAST SR |