TEKASTER™ F615G30FR
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | TEKASTER™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TvIrP2_TEKASTER-F615G30FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| F615G30FR is GF30% reinforced polyethylene terephthalate (PET). F615G30FR has good properties with flammability UL94 V_0 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.67 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 147 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 2.3 | % | ASTM D638 |
| Flexural Modulus 3 | 10100 | MPa | ASTM D790 |
| Flexural Strength 4 | 226 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 78 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 246 | °C | |
| 1.8 MPa, Unannealed | 224 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Rear Temperature | 245 to 255 | °C | |
| Middle Temperature | 250 to 260 | °C | |
| Front Temperature | 255 to 265 | °C | |
| Nozzle Temperature | 255 to 265 | °C | |
| Processing (Melt) Temp | 255 to 265 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD A 2800-75A | RTP Company | TPO (POE) | RTP |
| Mirakutoran® TPU E670MZAA | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Bergamid™ B70 G60 H BK037 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| EPALINE 392A11 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPALINE |
| LNP™ THERMOCOMP™ MF002AS compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |