RTV-2 GI-1120
| Category: | Silicone Rubber, RTV-2 , Silicone Rubber, RTV-2 |
| Manufacturer: | Silicones, Inc. |
| Trademark: | RTV-2 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Tup85b_RTV-2-GI-1120.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GI-1120 is a high tear strength, tin-catalyzed RTV-2 silicone rubber, which was designed for casting polyester parts. GI-1120 is especially good for molds with deep undercuts and for molds that require flexing for part removal. GI-1120 is not sensitive to inhibition, meaning it will cure at room temperature over virtually any surface. It is easy to mix and de-air, and will cure with only a slight degree of shrinkage. The speed at which the rubber hardens can beaccelerated with special activators. Condensation cure two-component silicone rubbers are excellent for most general mold making and prototype applications. They are excellent for casting waxes, gypsum, epoxies and other plastics. GI-1120 is extremely useful for those applications where superior elongation and medium durometer are required. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | |
| Shrinkage - Cured | 0.10 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature - Cured | -51 to 171 | °C |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coverage - Cured | 0.925 | cm³/g |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 11 Mix Ratio by Weight: 1.0 | ||
| Resin | Mix Ratio by Weight: 10 Mix Ratio by Volume: 100 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity | 25000 to 35000 | cP |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 1 | Blue | ||
| -- 2 | Off White | ||
| Viscosity | |||
| -- 3 | 0.30 to 0.40 | Pa·s | |
| -- 4 | 45 to 55 | Pa·s | |
| Curing Time | 16 to 18 | hr | |
| Pot Life | 90 to 150 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | |||
| Shore A 5 | 11 to 19 | ||
| Shore A 6 | 16 to 24 | ||
| Tensile Strength | 2.52 to 2.86 | MPa | ASTM D412 |
| Tensile Elongation at Break | 450 to 500 | % | ASTM D412 |
| Tear Strength | 14.9 to 18.4 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Activator |
| 2 . | Base |
| 3 . | Activator |
| 4 . | Base |
| 5 . | 1 Day |
| 6 . | 7 Days |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Menzolit® BMC 1500 | Menzolit Ltd (UK) | Polyester, TS | Menzolit® |
| Trexprene® A45BU | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| Arnite® TV4 660 SN | DSM Engineering Plastics | PC+PBT | Arnite® |
| ICORENE® 1506 | A. Schulman Europe | XLPE | ICORENE® |
| Rotuba CAP CP808 (16% Plasticizer) | Rotuba Extruders, Inc. | CAP | Rotuba CAP |