TARFLON™ G1920
| Category: | PC , Polycarbonate |
| Manufacturer: | Idemitsu Kosan Co., Ltd. |
| Trademark: | TARFLON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TuhsWu_TARFLON-G1920.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Basic |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ISO 1183 |
| Spiral Flow | 18.0 | cm | Internal Method |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 2.00 mm | 0.60 | % | |
| Flow : 2.00 mm | 0.20 | % | |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.13 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 70 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 110 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 5900 | MPa | ISO 178 |
| Flexural Stress | 160 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 145 | °C | ISO 75-2/A |
| CLTE - Flow | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Electric Strength | > 22 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.15 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 9.0E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.700 mm) | HB | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| ISO Shortname | >PC-GF20< |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 5.0 to 8.0 | hr | |
| Rear Temperature | 260 to 300 | °C | |
| Middle Temperature | 260 to 300 | °C | |
| Front Temperature | 260 to 300 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 24h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| R-master® 92200 | Polimeros Mexicanos s.a. de c.v. | LLDPE | R-master® |
| AIE PBT 30G8F | Asia International Enterprise (Hong Kong) Limited | PBT | AIE PBT |
| Karina ORANGE PVC COMPOUND 650-32/95 (MP-1.0) (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LOXIM 330 01 HB | LOXIM Industries Private Limited | Nylon 6 | LOXIM |
| PLUSTEK PB351I6 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |