RTV-2 GI-311B
| Category: | Silicone Rubber, RTV-2 , Silicone Rubber, RTV-2 |
| Manufacturer: | Silicones, Inc. |
| Trademark: | RTV-2 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TueWAY_RTV-2-GI-311B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GI-300 series RTV silicone rubbers are two-component, tin-catalyzed systems that cure at room temperature. They are versatile products that are excellent for electrical potting and encapsulation. They can also be used for prototype or production molds to cast polyester, polyurethane or epoxy parts where flexing is not required. They are low viscosity compounds with a variety of hardnesses. The GI-300 series rubbers are not sensitive to inhibition, meaning they will cure at room temperature over virtually any surface. The speed at which the rubbers harden can be accelerated with special activators. The GI-300 series rubbers are especially useful in those applications where outstanding heat resistance and chemical resistance are required. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | |
| Shrinkage - Cured | 0.25 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature - Cured | -51 to 218 | °C |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coverage - Cured | 0.878 | cm³/g |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE - Flow | 1.1E-3 | cm/cm/°C | |
| Thermal Conductivity | 0.21 | W/m/K |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 1.0 Mix Ratio by Volume: 12 | ||
| Resin | Mix Ratio by Weight: 10 Mix Ratio by Volume: 100 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity 1 | 3000 to 13000 | cP |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color 2 | Beige | ||
| Viscosity 3 | 9.0 to 19 | Pa·s | |
| Curing Time | 16 to 18 | hr | |
| Pot Life | 60 to 120 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | |||
| Shore A 4 | 38 to 46 | ||
| Shore A 5 | 40 to 48 | ||
| Tensile Strength | 2.24 | MPa | ASTM D412 |
| Tensile Elongation at Break | 150 | % | ASTM D412 |
| Tear Strength | 3.50 | kN/m | ASTM D624 |
| Arc Resistance | 90.0 | sec | |
| Electric Strength | 23 | kV/mm | |
| Relative Permittivity (100 Hz) | 3.00 | ||
| Volume Resistivity | 1.0E+13 | ohms·cm | |
| Dissipation Factor (100 Hz) | 0.010 |
| Note Message | |
|---|---|
| 1 . | Mixed |
| 2 . | Base |
| 3 . | Base |
| 4 . | 1 Day |
| 5 . | 7 Days |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Salflex 620TIC | Salflex Polymers Ltd. | PP Copolymer | Salflex |
| Tufpet PBT G1030 | Mitsubishi Rayon America Inc. | PBT | Tufpet |
| ALCUDIA® LDPE 2008-F | REPSOL | LDPE | ALCUDIA® LDPE |
| HAIPLEN EP50 C6 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| LNP™ THERMOCOMP™ IF006L compound | SABIC Innovative Plastics | Nylon 612 | LNP™ THERMOCOMP™ |