Amilan® CM1016G-30
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Toray Resin Company |
| Trademark: | Amilan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TuduGp_Amilan-CM1016G-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Amilan® CM1016G-30 is a Polyamide 6 (Nylon 6) product filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Part Marking Code |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.36 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow : 3.00 mm 1 | 0.50 to 0.80 | -- | % | |
| Flow : 3.00 mm 2 | 0.20 to 0.40 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 1.1 | -- | % | |
| Saturation, 23°C | 6.4 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | |||
| M-Scale, 23°C | 93 | -- | ||
| R-Scale, 23°C | 120 | -- | ||
| R-Scale, 80°C | 12 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress | ISO 527-2 | |||
| -40°C | 250 | 225 | MPa | |
| 23°C | 185 | 105 | MPa | |
| 80°C | 100 | 70.0 | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break, -40°C | 3.0 | 3.0 | % | |
| Break, 23°C | 3.0 | 4.0 | % | |
| Break, 80°C | 4.0 | 4.5 | % | |
| Flexural Modulus | ISO 178 | |||
| -40°C | 11800 | 9800 | MPa | |
| 23°C | 9500 | 5100 | MPa | |
| 80°C | 4700 | 3500 | MPa | |
| Flexural Stress | ISO 178 | |||
| -40°C | 325 | 315 | MPa | |
| 23°C | 280 | 145 | MPa | |
| 80°C | 155 | 105 | MPa | |
| Compressive Stress | ISO 604 | |||
| -40°C | 250 | 210 | MPa | |
| 23°C | 180 | 120 | MPa | |
| 80°C | 95.0 | 70.0 | MPa | |
| Shear Strength (23°C) | 85.0 | -- | MPa | ASTM D732 |
| Taber Abrasion Resistance (1000 Cycles) | 0.350 | -- | mg | ISO 9352 |
| Coefficient of Friction - vs. Metal 3 | 0.150 | -- | Suzuki Method |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -40°C | 10 | 17 | kJ/m² | |
| 23°C | 15 | 23 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -40°C | 70 | 80 | kJ/m² | |
| 23°C | 80 | 100 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 224 | -- | °C | ISO 75-2/B |
| Melting Temperature | 225 | -- | °C | DSC |
| CLTE - Flow | 2.0E-5 to 3.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1600 | -- | J/kg/°C | |
| Thermal Conductivity | 0.38 | -- | W/m/K |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 20 | 18 | kV/mm | IEC 60243-1 |
| Dielectric Constant 4 | IEC 60250 | |||
| 23°C, 50 Hz | 4.90 | 10.7 | ||
| 23°C, 1 kHz | 4.60 | 7.90 | ||
| 23°C, 1 MHz | 4.00 | 4.30 | ||
| Dissipation Factor 5 | IEC 60250 | |||
| 23°C, 50 Hz | 0.030 | 0.17 | ||
| 23°C, 1 kHz | 0.030 | 0.18 | ||
| 23°C, 1 MHz | 0.030 | 0.070 | ||
| Arc Resistance 6 | 131 | 137 | sec | UL 746 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.794 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | Without Lubrication |
| 4 . | 60% RH |
| 5 . | 60% RH |
| 6 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| METLBOND® 2550 | Cytec Industries Inc. | MAH-g | METLBOND® |
| Mirakutoran® TPU E585 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Moplen RP225M | LyondellBasell Industries | PP Random Copolymer | Moplen |
| Geon™ Fiberloc™ 80510 | PolyOne Corporation | PVC, Rigid | Geon™ Fiberloc™ |
| Vydyne® 66J NT0692 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |