TIPELIN® 7000F
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | MOL Petrochemicals Co. Ltd. |
| Trademark: | TIPELIN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TtgGbB_TIPELIN-7000F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TIPELIN 7000F is a high density bimodal polyethylene copolymer (with butene-1 as comonomer) intended for blown film of products with excellent mechanical strength and good stiffness. It offers good processability at high speed. The grade contains antioxidant and acid scavenger. Applications TIPELIN 7000F is recommended for disposal waste bags, grocery bags and ultra-thin films. TIPELIN 7000F is suitable for food contact and for manufacturing of pharmaceutical packing products. The product complies with Food Contact and Pharmaceutical Regulations. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.955 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.080 | g/10 min | |
| 190°C/21.6 kg | 9.0 | g/10 min | |
| 190°C/5.0 kg | 0.30 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 64 | ISO 868 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 15 µm, Blown Film | 26.0 | MPa | |
| TD : Yield, 15 µm, Blown Film | 25.0 | MPa | |
| MD : Break, 15 µm, Blown Film | 67.0 | MPa | |
| TD : Break, 15 µm, Blown Film | 50.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 15 µm, Blown Film | 500 | % | |
| TD : Break, 15 µm, Blown Film | 600 | % | |
| Dart Drop Impact (15 µm, Blown Film) | 240 | g | ISO 7765-1/A |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 15 µm, Blown Film | 0.15 | N | |
| TD : 15 µm, Blown Film | 1.5 | N | |
| Spencer Impact - Blown Film (15.0 µm) | 120 | MPa | ASTM D3420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (200°C) | 45 | min | EN 728 |
| Vicat Softening Temperature | 126 | °C | ISO 306/A120 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 to 165 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECOLITE KM-2000(G) | KYOCERA Chemical Corporation | Phenolic | TECOLITE |
| Sylvin 8311-70D Natural | Sylvin Technologies Incorporated | PVC, Semi-Rigid | Sylvin |
| Borealis PP RF926MO | Borealis AG | PP Random Copolymer | Borealis PP |
| CYROVU® HP2 | Evonik Cyro LLC | Acrylic (PMMA) | CYROVU® |
| Capilene® QC 71 E | Carmel Olefins Ltd. | PP Random Copolymer | Capilene® |