ACRYPET® VHM
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Lucite International Holland BV |
| Trademark: | ACRYPET® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Tsf8sY_ACRYPETVHM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACRYPET®VHM is a polymethyl methacrylate-acrylic material,. This product is available in Europe,. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 3.1 | g/10 min | ISO 1133 |
| Spiral Flow | Internal method | ||
| -- 1 | 14.0 | cm | Internal method |
| -- 2 | 23.0 | cm | Internal method |
| Molding Shrinkage | 0.20 - 0.60 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 101 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 76.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus | 3300 | MPa | ISO 178 |
| Flexural Stress | 135 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 1.4 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 20 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 100 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 107 | °C | ISO 306/B |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | 1500 | J/kg/°C | JIS K7123 |
| Thermal Conductivity | 0.20 | W/m/K | ASTM C177 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ASTM D542 | |
| Transmittance (Total, 3000 µm) | 93.0 | % | ISO 13468 |
| Haze (3000 µm) | 0.30 | % | ISO 14782 |
| Note Message | |
|---|---|
| 1 . | Melt temperature: 230°C |
| 2 . | Melt temperature: 250°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRILAC AG15A1-H | Formosa Plastics Corporation | ABS | TAIRILAC |
| Exxtral™ Performance Polyolefin CMV206 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| Sylvin 5170-85 Red 6290 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Monprene® CP-15140D-10 NAT XRD1 | Teknor Apex Company | TPE | Monprene® |
| LEXAN™ 943X resin | SABIC Innovative Plastics | PC | LEXAN™ |