TECACOMP® PA66 TC white 4040
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ensinger GmbH |
| Trademark: | TECACOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Trkz3T_TECACOMPPA66TCwhite4040.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Main features
Target Industries
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.87 | g/cm³ | |
| Apparent Density | 0.85 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 58 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 85.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 1.3 | % | ISO 294-4 |
| Flow | 1.3 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.5 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7600 | MPa | ISO 527-2/50 |
| Tensile Stress | 80.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 20 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 183 | °C | ISO 75-2/A |
| Glass Transition Temperature | 50.0 | °C | DIN 53765 |
| Melting Temperature | 255 | °C | DIN 53765 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 45°C | 7.3E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 70 to 120°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 23 to 45°C | 6.9E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 70 to 120°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1280 | J/kg/°C | DIN EN 821 |
| Thermal Conductivity | DIN EN 821 | ||
| -- 1 | 1.3 | W/m/K | DIN EN 821 |
| -- 2 | 1.4 | W/m/K | DIN EN 821 |
| Service Temperature | |||
| long term | 110 | °C | |
| short term | 170 | °C | |
| Thermal Diffusivity | DIN EN 821 | ||
| In-plane | 0.600 | cSt | DIN EN 821 |
| Through-plane | 0.600 | cSt | DIN EN 821 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 4.8E+12 | ohms | DIN EN 61340 |
| Volume Resistivity | 4.2E+13 | ohms·cm | DIN EN 61340 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | HB | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Processing (Melt) Temp | 260 - 295 | °C | |
| Mold Temperature | 100 - 150 | °C |
| Note Message | |
|---|---|
| 1 . | Through-plane |
| 2 . | In-plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TES AC-80/GB/20/M BK | Techmer Engineered Solutions | Acetal (POM) Copolymer | TES |
| Celstran® PA66-GF60-02 P11/14 | Celanese Corporation | Nylon 66 | Celstran® |
| Delrin® 100TE NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Infino UF-1013 | SAMSUNG SDI CO., LTD. | PC | Infino |
| LubriOne™ PC-30GF/15T BLACK | PolyOne Corporation | PC | LubriOne™ |