Novalloy-E E50
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Novalloy-E |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TrA7M1_Novalloy-E-E50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Novalloy-E E50 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific. Primary attribute of Novalloy-E E50: Flame Rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (240°C/5.0 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 37.0 | MPa | ISO 527-2 |
| Flexural Modulus | 1800 | MPa | ISO 178 |
| Flexural Stress | 56.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 12 | kJ/m² | |
| Notched Izod Impact (23°C, 6.40 mm) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 12.7 mm | 90.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 80.0 | °C | ISO 75-2/A |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 6.0E+12 | ohms | ASTM D257 |
| Dielectric Strength (1.50 mm) | 11 | kV/mm | ASTM D149 |
| Arc Resistance (3.00 mm) | 57.0 | sec | ASTM D495 |
| Arc Resistance (3.00 mm) | PLC 7 | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | V-2 | ||
| 1.50 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Rear Temperature | 180 to 200 | °C | |
| Middle Temperature | 210 to 220 | °C | |
| Front Temperature | 220 to 230 | °C | |
| Nozzle Temperature | 210 to 220 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Back Pressure | 10.0 to 20.0 | MPa | |
| Screw Speed | 60 to 90 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AT0320GN | Ginar Technology Co., LTD. | Nylon 66 | Mapex |
| RTP 283 A TFE 10 | RTP Company | Nylon 6 | RTP |
| Tenac™-C ZLV40 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| LNP™ STAT-KON™ DX05042 compound | SABIC Innovative Plastics Europe | PC | LNP™ STAT-KON™ |
| LUVOCOM® 1/XCF/40 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |