LUVOCOM® 65-8961/ES Datasheet,PP Copolymer,LEHVOSS Group-SHANGHAI SUSHENG

Message
LUVOCOM®65-8961/ES is a polypropylene copolymer (PP Copoly) material, which contains stainless steel fiber. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 65-8961/ES are: Conductivity Electromagnetic shielding (EMI)

General Information
Filler / Reinforcement	Stainless steel fiber
Features	Conductivity Electromagnetic shielding (EMI) Static conduction
Appearance	Black

Physical	Nominal Value	Unit	Test Method
Density	1.20	g/cm³	ISO 1183
Molding Shrinkage	1.0 - 1.6	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.10	%

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	74		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2500	MPa	ISO 527-2
Tensile Stress (Break)	33.0	MPa	ISO 527-2
Tensile Strain (Yield)	4.9	%	ISO 527-2
Flexural Modulus	2000	MPa	ISO 178
Flexural Stress	46.0	MPa	ISO 178
Flexural Strain at Flexural Strength	6.5	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	110	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	1.0 - 3.2	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength
-30°C	27	kJ/m²	ISO 179/1fU
23°C	29	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	59.0	°C	ISO 75-2/A
Continuous Use Temperature	80.0	°C	UL 746B
Vicat Softening Temperature	150	°C	ISO 306/A

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	< 10	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature - Desiccant Dryer	70 - 95	°C
Drying Time - Desiccant Dryer	2.0 - 4.0	hr
Rear Temperature	220 - 250	°C
Middle Temperature	220 - 250	°C
Front Temperature	230 - 260	°C
Nozzle Temperature	220 - 250	°C
Processing (Melt) Temp	230 - 260	°C
Mold Temperature	40 - 80	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.2%. Moisture may lead to smearing and in extreme cases to foaming. Usually the material can be processed over a broad temperature range and can thus be adapted to a wide variety of processing conditions. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.2%. Moisture may lead to smearing and in extreme cases to foaming. Usually the material can be processed over a broad temperature range and can thus be adapted to a wide variety of processing conditions. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	PP Copolymer , Polypropylene Copolymer
Manufacturer:	LEHVOSS Group
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Tr5ogv_LUVOCOM658961ES.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 205 TFE 15 EG	RTP Company	Nylon 66	RTP
Zhongfa POM GR-30	Yuyao Zhongfa Engineering Plastics Co. Ltd.	Acetal (POM) Copolymer	Zhongfa
Nipol® 1043	Zeon Chemicals L.P.	NBR	Nipol®
HiFill® PEEK CF40 HF	Techmer Engineered Solutions	PEEK	HiFill®
Kingfa MAC-501	Kingfa	PC+ABS	Kingfa