| 40% GLASS FIBER REINFORCED, LINEAR POLYPHENYLENE SULFIDE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.66 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 to 0.40 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.040 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 148 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 to 3.0 | % | ASTM D638 |
| Flexural Modulus | 14500 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 96 | J/m | ASTM D256 |
| Unnotched Izod Impact | 530 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 260 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 321 to 332 | °C | |
| Mold Temperature | 135 to 177 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 7.6E-3 to 0.013 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4605 TFE 10 | RTP Company | SPS | RTP |
| Rhelon G2533H-01 | RheTech, Inc. | Nylon 66 | Rhelon |
| Sumikon® PM-6930H | Sumitomo Bakelite Co., Ltd. | Phenolic | Sumikon® |
| ALTECH® PA6 A 2030/587 GF30 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| MAJORIS BG208 - 7731 | AD majoris | PP, Unspecified | MAJORIS |