NOVAPOL® HF-W952-A
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | NOVA Chemicals |
| Trademark: | NOVAPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TpWZz3_NOVAPOL-HF-W952-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NOVAPOL® HF-W952-A is a High Density Polyethylene material. It is available in North America for film extrusion. Important attributes of NOVAPOL® HF-W952-A are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.952 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 10 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 18 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 18 µm, Blown Film | 746 | MPa | |
| 1% Secant, TD : 18 µm, Blown Film | 884 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 18 µm, Blown Film | 27.0 | MPa | |
| TD : Yield, 18 µm, Blown Film | 26.0 | MPa | |
| MD : Break, 18 µm, Blown Film | 50.0 | MPa | |
| TD : Break, 18 µm, Blown Film | 44.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 18 µm, Blown Film | 470 | % | |
| TD : Break, 18 µm, Blown Film | 580 | % | |
| Dart Drop Impact (18 µm, Blown Film) | 83 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 18 µm, Blown Film | 16 | g | |
| TD : 18 µm, Blown Film | 79 | g |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Low Friction Puncture 1(18.0 µm) | 260 | J/cm | Internal Method |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermylene® P6-25FG-0687 | Asahi Kasei Plastics North America Inc. | PP, Unspecified | Thermylene® |
| NYLOY® UB-0010N G60N1N | Nytex Composites Co., Ltd. | Nylon, Unspecified | NYLOY® |
| Formolene® 4101O | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| Sylvin 6168-80 Grey 9552 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| 3M™ Dyneon™ PTFE Compound TF 3406 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |