Electrafil® PC 03906 MB
| Category: | PC , Polycarbonate |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Electrafil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TotuGB_Electrafil-PC-03906-MB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Electrafil®PC 03906 MB is a polycarbonate (PC) product,. It can be processed by injection molding and is available in North America. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.12 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 49.0 | MPa | ASTM D638 |
| Fracture | 51.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 2620 | MPa | ASTM D790 |
| Flexural Strength | 86.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.18 mm) | 440 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 138 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 129 | °C | ASTM D648 |
| CLTE - Flow | 5.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 10 | ohms | ASTM D257 |
| Volume Resistivity | < 10 | ohms·cm | ASTM D257 |
| Static Decay | FTMS 101B | ||
| Shielding Effectiveness - 30 to 1000 MHz | -30 | dB | ASTM D4935 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 302 - 316 | °C | |
| Middle Temperature | 316 - 332 | °C | |
| Front Temperature | 310 - 327 | °C | |
| Nozzle Temperature | 310 - 327 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 71.1 - 87.8 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.00 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw Speed: MediumRecommendations for Molding and Tool Conditions: Well vented moldMoisture Content, as received: Product is packaged at 0.2% or less. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirathane™ E260 | Miracll Chemicals Co., Ltd. | TPU-Polyester | Mirathane™ |
| tefanyl® VE VEIP 206 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | tefanyl® VE |
| NEXT REGRIND PBT DR51-100RG | NEXT Specialty Resins, Inc. | PBT | NEXT REGRIND |
| 4LOY® 10E17300 | 4Plas | PC+ABS | 4LOY® |
| Globalprene® 3412P | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |