AKROMID® B3 GM 10/20 1 L black (4646)
| Category: | Nylon 6+PP , Polyamide 6 + PP |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | To5OET_AKROMID-B3-GM-10-20-1-L-black-4646-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 GM 10/20 1 L black (4646) is a 10% glass fibre reinforced, 20% glass bead filled and heat stabilised polyamide-blend with a reduced density compared to standard PA6 GF10 + GB20 Applications are mainly optical components in the automotive and electronic industry, where a weight and cost reduction is required |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.26 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 18.0 | -- | cm³/10min | ISO 1133 |
| Spiral Flow | 73.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.2 | -- | % | |
| Flow | 0.50 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 1.4 | -- | % | ISO 1110 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 30 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5100 | 3300 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 88.0 | 55.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.4 | 6.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 4700 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 130 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | 4.0 | kJ/m² | |
| 23°C | 7.0 | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 43 | 42 | kJ/m² | |
| 23°C | 46 | 44 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 208 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 165 | -- | °C | ISO 75-2/A |
| Melting Temperature 3 | 220 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecodur® PB70 GR10 NL100 | Eurotec Engineering Plastics | PBT | Tecodur® |
| Spherisil P 23-08670 | SILON s.ro | PE, Unspecified | Spherisil |
| TRANSMARE® 35HT40-0.001 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| ALFATER XL® A90I 2GP0050 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |
| Karina WHITE PVC COMPOUND 800-10/AY-RT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |