HiFill® PA6 GF50 L
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Tnb9og_HiFill-PA6-GF50-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiFill® PA6 GF50 L is a Polyamide 6 (Nylon 6) product filled with 50% glass fiber. It can be processed by injection molding and is available in North America. Primary characteristic: lubricated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.57 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | -- | % | ASTM D955 |
| Water Absorption (24 hr) | 0.75 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength (Break) | 221 | 193 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | 4.0 | % | ASTM D638 |
| Flexural Modulus | 14100 | 10700 | MPa | ASTM D790 |
| Flexural Strength | 290 | 269 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 160 | 270 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 1100 J/m | No Break | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 218 | -- | °C | |
| 1.8 MPa, Unannealed | 216 | -- | °C | |
| CLTE - Flow | 1.4E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 18 | -- | kV/mm | ASTM D149 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 260 to 304 | °C | |
| Middle Temperature | 260 to 304 | °C | |
| Front Temperature | 260 to 304 | °C | |
| Processing (Melt) Temp | 243 to 271 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.00 to 0.345 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Topilene® HB240P | Hyosung Corporation | PP Impact Copolymer | Topilene® |
| Titalon® 2330GMS | Titan Plastics Compounds Co., Ltd. | Nylon 66 | Titalon® |
| Vi-Chem PVC VNC87-5E | Vi-Chem Corporation | PVC, Flexible | Vi-Chem PVC |
| Hostacom EKC 265N 2 C12594 | LyondellBasell Industries | PP Copolymer | Hostacom |
| AA-Recoplast A3H1 | SmartLab Latvia SIA | PE, Unspecified | AA-Recoplast |