Infino NH-1027HF
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TnYmtf_Infino-NH-1027HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino NH-1027HF is a Polycarbonate + ABS (PC+ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 55 | g/10 min | ASTM D1238, ISO 1133 |
| Water Absorption | |||
| 23°C, 24 hr | 0.20 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 60.0 | MPa | ASTM D638 |
| Yield | 67.0 | MPa | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 2400 | MPa | ASTM D790 |
| -- 3 | 2550 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 88.0 | MPa | ASTM D790 |
| -- 5 | 89.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6(23°C) | 17 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 540 | J/m | ASTM D256 |
| 23°C 7 | 14 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 98.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | V-1 | ||
| 1.20 mm | V-0 | ||
| 1.50 mm | V-0 5VB | ||
| 3.00 mm | V-0 5VB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 85.0 | °C | |
| Desiccant Dryer | 85.0 | °C | |
| Drying Time | |||
| -- | 2.0 | hr | |
| Desiccant Dryer | 2.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Rear Temperature | 235 to 245 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 245 to 255 | °C | |
| Nozzle Temperature | 250 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 98.1 | MPa | |
| Back Pressure | 0.490 to 2.94 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Thickness: 4 mm |
| 7 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXNITE® PET 500 GF15 | MRC Polymers, Inc. | PET | MAXNITE® PET |
| RapidVac™ VA-1810 | Innovative Polymers, Inc. | TSU | RapidVac™ |
| Somos® BioClear | DSM Somos® | Unspecified | Somos® |
| PENTAMID AB SK H natur | PENTAC Polymer GmbH | Nylon 66/6 | PENTAMID AB |
| Polifor® E 8 TR/30 UV GRIGIO 7061 (648) | SO.F.TER. SPA | PP Copolymer | Polifor® |