VICTREX® HT™ 22GL30
| Category: | PEK , Polyether Ketone |
| Manufacturer: | Victrex plc |
| Trademark: | VICTREX® HT™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Tmhfgi_VICTREX-HT-22GL30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High performance thermoplastic material, 30% glass fibre reinforced PolyEtherKetone (PEK), semi crystalline, granules for injection moulding, standard flow, colour natural/beige. Higher temperature applications where higher strength in a static system is required. Low coefficient of thermal expansion. Chemically resistant to aggressive environments, suitable for sterilisation for medical and food contact applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.53 | g/cm³ | ISO 1183 |
| Spiral Flow | 10.5 | cm | Internal method |
| Molding Shrinkage 2 | ISO 294-4 | ||
| Vertical flow direction | 0.90 | % | ISO 294-4 |
| Flow direction | 0.30 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 3.20 mm | 0.050 | % | ISO 62 |
| Saturated, 23°C, 3.20mm | 0.50 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 88 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 12000 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Fracture, 23°C | 200 | MPa | ISO 527-2 |
| Fracture, 125°C | 125 | MPa | ISO 527-2 |
| Fracture, 175°C | 75.0 | MPa | ISO 527-2 |
| Fracture, 225°C | 65.0 | MPa | ISO 527-2 |
| Fracture, 275°C | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.8 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 11000 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| 23°C | 300 | MPa | ISO 178 |
| 125°C | 210 | MPa | ISO 178 |
| 175°C | 120 | MPa | ISO 178 |
| 275°C | 85.0 | MPa | ISO 178 |
| Compressive Stress | ISO 604 | ||
| 23°C | 290 | MPa | ISO 604 |
| 120°C | 180 | MPa | ISO 604 |
| 200°C | 75.0 | MPa | ISO 604 |
| 250°C | 50.0 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 70 | kJ/m² | ISO 179/1U |
| Notched Izod Impact (23°C) | 11 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength (23°C) | 70 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 360 | °C | ISO 75-2/Ae |
| Glass Transition Temperature | 152 | °C | ISO 11357-2 |
| Melting Temperature | 373 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : < 152°C | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : > 152°C | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : < 152°C | 4.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : > 152°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Specific Heat (23°C) | 1700 | J/kg/°C | DSC |
| Thermal Conductivity (23°C) | 0.30 | W/m/K | ISO 22007-4 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | 23 | kV/mm | IEC 60243-1 |
| Dielectric Constant (23°C, 1 kHz) | 3.20 | IEC 60250 | |
| Dissipation Factor (23°C, 1 MHz) | 5.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (400°C) | 500 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Hopper Temperature | < 100 | °C | |
| Rear Temperature | 375 | °C | |
| Middle Temperature | 380 - 385 | °C | |
| Front Temperature | 390 | °C | |
| Nozzle Temperature | 395 | °C | |
| Mold Temperature | 190 - 215 | °C |
| Injection instructions |
|---|
| Runner: Die / nozzle >3mm, manifold >3.5mmGate: >2mm or 0.5 x part thickness |
| Note Message | |
|---|---|
| 1 . | Crystalline |
| 2 . | 395°C nozzle, 200°C tool |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NYCOA Polyamide 2612 | Nycoa (Nylon Corporation of America) | Nylon 612 | NYCOA Polyamide |
| Cereplast Hybrid Resins® 101 | Cereplast, Inc. | PP Alloy | Cereplast Hybrid Resins® |
| Fainplast PVC MGS 91/T | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Geon™ Vinyl Flexible A8000 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| POCAN® KL 1-7265 POS151 901317 | LANXESS GmbH | PBT | POCAN® |