Daelim Po1y® LH6070T
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | DAELIM INDUSTRIAL CO., LTD. |
| Trademark: | Daelim Po1y® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TmHh1G_Daelim-Po1y-LH6070T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Daelim Po1y® LH6070T is a High Density Polyethylene product. It can be processed by injection molding and is available in Asia Pacific. Applications of Daelim Po1y® LH6070T include consumer goods and food contact applications. Primary characteristic: food contact acceptable. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.961 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.020 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 60 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 28.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 700 | % | ASTM D638 |
| Flexural Modulus | 1080 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Purell PE 1840 H | LyondellBasell Industries | LDPE | Purell |
| NORYL™ FXN121BK resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| FRIANYL® A3 GF25 V0XI | Nilit Plastics | Nylon 66 | FRIANYL® |
| Lumid® GP2200B(W) | LG Chem Ltd. | Nylon 66 | Lumid® |
| Polyclear® Refresh PET 1101 | Indorama Ventures Polymers México | PET | Polyclear® |