VALOX™ V3500EX resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Tm9OEd_VALOX-V3500EX-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unfilled PBT,Flame Retardant, good flow, high elongation at break for Extrusion applications (Monofilaments, Insulation Cables),Electrical Parts and Connectors |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 265°C/5.0 kg | 50 | g/10 min | |
| 266°C/5.0 kg | 50 | g/10 min | |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/2.16 kg | 13.0 | cm³/10min | |
| 250°C/5.0 kg | 13.0 | cm³/10min | |
| 265°C/5.0 kg | 40.0 | cm³/10min | |
| Molding Shrinkage 1 | Internal Method | ||
| Flow | 1.1 to 1.8 | % | |
| Across Flow | 0.90 to 1.8 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.35 | % | |
| Equilibrium, 23°C, 50% RH | 0.080 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 170 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 3100 | MPa | ASTM D638 |
| -- | 3200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 60.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Break 4 | 40.0 | MPa | ASTM D638 |
| Break | 50.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 5 | 3.0 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2/50 |
| Break 6 | 15 | % | ASTM D638 |
| Break | > 70 | % | ISO 527-2/50 |
| Flexural Modulus 7 | 2850 | MPa | ISO 178 |
| Flexural Stress | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C | 5.0 | kJ/m² | ISO 179/2C |
| 23°C 8 | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 6.0 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength | ISO 179/2U | ||
| -30°C | 80 | kJ/m² | |
| 23°C | 95 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 40 | J/m | ASTM D256 |
| 0°C | 40 | J/m | ASTM D256 |
| 23°C | 40 | J/m | ASTM D256 |
| -30°C 9 | 6.0 | kJ/m² | ISO 180/1A |
| 0°C 10 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -30°C | 830 | J/m | ASTM D4812 |
| 23°C | 950 | J/m | ASTM D4812 |
| -30°C 12 | 60 | kJ/m² | ISO 180/1U |
| 23°C 13 | 60 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 165 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 14 | 165 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 80.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 15 | 80.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 220 | °C | ASTM D1525, ISO 306/A50 11 16 |
| -- | 180 | °C | ASTM D1525, ISO 306/B50, ISO 306/B120 17 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.0E-5 | cm/cm/°C | |
| Flow : 23 to 150°C | 1.9E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.4E-5 | cm/cm/°C | |
| Transverse : 23 to 150°C | 1.4E-4 | cm/cm/°C | |
| RTI Elec | 75.0 | °C | UL 746 |
| RTI Imp | 75.0 | °C | UL 746 |
| RTI Str | 75.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | |||
| 1.60 mm, in Oil | 39 | kV/mm | ASTM D149, IEC 60243-1 |
| 3.20 mm, in Oil | 21 | kV/mm | ASTM D149, IEC 60243-1 |
| 0.800 mm, in Oil | 62 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 2.90 | ASTM D150, IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.016 | ASTM D150, IEC 60250 | |
| Comparative Tracking Index | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm, Testing by SABIC) | V-0 | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (260°C, 1500 sec^-1) | 170 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 230 to 245 | °C | |
| Middle Temperature | 240 to 255 | °C | |
| Front Temperature | 245 to 265 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 40.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | Type I, 50 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 sp=62mm |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 mm |
| 15 . | 80*10*4 mm |
| 16 . | Rate A (50°C/h), Loading 2 (50 N) |
| 17 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen BA238A | PolyMirae | PP Copolymer | Moplen |
| APEX® 1013 | Teknor Apex Company | PVC, Semi-Rigid | APEX® |
| Ferro PP LPP40BD12GY | Ferro Corporation | PP Homopolymer | Ferro PP |
| Sylvin 6185-80 Grey 9132 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| INVISION™ GX 5090-G6U-3120 BLACK WPT | A. Schulman Europe | TPE | INVISION™ |