LNP™ THERMOCOMP™ Noryl_HM4025 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Tm7pzk_LNPTHERMOCOMPNorylHM4025compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP THERMOCOMP NORYL_HM4025 compound is a 40% Glass/Mineral filled high modulus grade. DTUL 255F (124C). UL94 V-0/V-1/5VA rated in black and gray only (see thicknesses). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.15 | % | Internal method |
| Transverse flow : 3.20mm | 0.25 | % | Internal method |
| Water Absorption (24 hr) | 0.060 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 127 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield) | 1.5 | % | ASTM D638 |
| Flexural Modulus 3(100 mm Span) | 9650 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 100 mm Span) | 159 | MPa | ASTM D790 |
| Poisson's Ratio | 0.38 | ASTM D638 | |
| Coefficient of Friction | ASTM D1894 | ||
| With steel-static | 0.42 | ASTM D1894 | |
| With Self-Static | 0.44 | ASTM D1894 | |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 35.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 124 | °C | ASTM D648 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 95°C | 2.2E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 95°C | 3.2E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+17 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm, in Air) | 25 | kV/mm | ASTM D149 |
| Arc Resistance 5 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.47 mm | V-1 | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| 2.51 mm | 5VA | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 - 110 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 - 70 | % | |
| Rear Temperature | 260 - 304 | °C | |
| Middle Temperature | 271 - 310 | °C | |
| Front Temperature | 282 - 316 | °C | |
| Nozzle Temperature | 293 - 316 | °C | |
| Processing (Melt) Temp | 293 - 316 | °C | |
| Mold Temperature | 76.7 - 104 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 20 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | 2.6 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radel® R-7625 | Solvay Specialty Polymers | PPSU | Radel® |
| Niche PPCM6BK | Niche Polymer, LLC | PP Copolymer | Niche |
| CYCOLAC™ INP108 resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |
| Hostacom PPU X9067HS G62514 | LyondellBasell Industries | PP Copolymer | Hostacom |
| 3M™ Dyneon™ PTFE Compound TF 7717 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |