CYCOLAC™ MG37EPX resin
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TlpZvb_CYCOLACMG37EPXresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ABS plating grade optimized for a broad processing window for both painted and plated applications. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 21 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.60 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2760 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 48.5 | MPa | ISO 527-2/5 |
| Fracture | 39.6 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 2.1 | % | ISO 527-2/5 |
| Fracture | 16 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 2480 | MPa | ISO 178 |
| Flexural Stress | 73.2 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2 | ISO 180/1A | ||
| -40°C | 6.2 | kJ/m² | ISO 180/1A |
| -30°C | 8.2 | kJ/m² | ISO 180/1A |
| 23°C | 23 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 64.0 mm Span) | 82.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 98.2 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 93.3 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 50 - 70 | % | |
| Rear Temperature | 216 - 229 | °C | |
| Middle Temperature | 232 - 243 | °C | |
| Front Temperature | 249 - 268 | °C | |
| Nozzle Temperature | 254 - 279 | °C | |
| Processing (Melt) Temp | 254 - 279 | °C | |
| Mold Temperature | 37.8 - 82.2 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 30 - 60 | rpm | |
| Vent Depth | 0.038 - 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rhelon G2020-00 | RheTech, Inc. | Nylon 66 | Rhelon |
| Titacon® SI902 | Titan Plastics Compounds Co., Ltd. | Acetal (POM) Copolymer | Titacon® |
| AKROMID® A3 GF 30 4 L black (4678) | AKRO-PLASTIC GmbH | Nylon 66+PP | AKROMID® |
| KEBATER® PBT BF115 | BARLOG plastics GmbH | PBT | KEBATER® |
| LNP™ STAT-KON™ QE002S compound | SABIC Innovative Plastics | Nylon 610 | LNP™ STAT-KON™ |