Badamid® PA610 GF30
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TkkpF7_Badamid-PA610-GF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Badamid® PA610 GF30 is a Polyamide 610 (Nylon 610) material filled with 30% glass fiber. It is available in Europe for injection molding. Primary attribute of Badamid® PA610 GF30: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.42 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 1.4 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.60 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus 1(23°C) | 7700 | 6200 | MPa | ISO 527-2/1 |
| Tensile Stress 2(Break, 23°C) | 150 | 130 | MPa | ISO 527-2/1A/5 |
| Tensile Strain 3(Break, 23°C) | 3.0 | 3.8 | % | ISO 527-2/5 |
| Flexural Stress 4(23°C) | 220 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 85 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 210 | -- | °C | ISO 75-2/B |
| Melting Temperature (DSC) 5 | 220 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity (1.00 mm) | 1.0E+12 | -- | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 30 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | Test Specimen accordng to ISO 3167, Type A |
| 5 . | 10 K/Min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUCOMP™ ASA002L | ACLO Compounders Inc. | ASA | ACCUCOMP™ |
| ELASTOSIL® M 4500 | Wacker Chemie AG | Silicone | ELASTOSIL® M |
| Plaslube® POM HO TL15 | Techmer Engineered Solutions | Acetal (POM) Homopolymer | Plaslube® |
| EVALENE® LLDPE LF10182 | JG Summit Petrochemical Corporation | LLDPE | EVALENE® LLDPE |
| LNP™ STAT-KON™ KE002 compound | SABIC Innovative Plastics Europe | Acetal (POM) Copolymer | LNP™ STAT-KON™ |