LNP™ THERMOCOMP™ DX09402 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TkI2Kx_LNP-THERMOCOMP-DX09402-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP DX09402 is a compound based on Polycarbonate containing Proprietary Filler(s). Also known as: LNP* THERMOCOMP* Compound DX09402 Product reorder name: DX09402 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.23 | g/cm³ | |
| -- | 1.22 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.50 | % | |
| Across Flow : 24 hr | 0.30 to 0.60 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.14 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.18 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2970 | MPa | ASTM D638 |
| -- | 2990 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 56.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/5 |
| Break 3 | 45.0 | MPa | ASTM D638 |
| Break | 47.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 5.3 | % | ASTM D638 |
| Yield | 5.1 | % | ISO 527-2/5 |
| Break 5 | 37 | % | ASTM D638 |
| Break | 21 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2810 | MPa | ASTM D790 |
| -- 7 | 2640 | MPa | ISO 178 |
| Flexural Stress | 81.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 430 | J/m | ASTM D256 |
| 23°C 8 | 30 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 2300 | J/m | ASTM D4812 |
| 23°C 9 | 200 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 41.9 | J | ASTM D3763 |
| -- | 43.8 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 138 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 136 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 129 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 125 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 5.4E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.8E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Multiuse Leostomer® LE-3190N | Riken Technos Corp. | TPU, Unspecified | Multiuse Leostomer® |
| APEX® RE 8223-NT | Teknor Apex Company | PVC, Rigid | APEX® |
| DOMAMID® 27 | DOMO Caproleuna GmbH | Nylon 6 | DOMAMID® |
| LG ABS HF380I | LG Chem Ltd. | ABS | LG ABS |
| TECHNYL® C 52G1 V25 GREY 2225 CF | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |