Message
PRELIMINARY DATA SHEET Omnix® 4050 is a 50% glass-fiber reinforced, high-performance polyamide (HPPA). It is particularly suited for replacing die-cast metal in a variety of mechanical applications and components used in automotive, consumer goods, E/E, and construction. Components injection molded from Omnix® 4050 display exceptional mechanical properties and excellent surface appearance even after moisture adsorption. Black: Omnix® 4050 BK 000 Natural: Omnix® 4050 NT 000

General Information
Features	Good dimensional stability Rigidity, high High strength Impact resistance, good Sprayable Fast molding cycle High liquidity Hot water formability Excellent appearance
Uses	Electrical/Electronic Applications Mechanical maintenance/repair Automotive Electronics
RoHS Compliance	RoHS compliance
Appearance	Black Natural color
Forms	Particle
Processing Method	Water temperature mold injection molding Injection molding
Part Marking Code (ISO 11469)	>(PA+PPA)-GF50

Physical	Dry	Conditioned	Unit	Test Method
Specific Gravity	1.59	--	g/cm³	ASTM D792
Molding Shrinkage ¹				ISO 294-4
Vertical flow direction	0.50	--	%	ISO 294-4
Flow direction	0.10	--	%	ISO 294-4

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	17000	--	MPa	ISO 527-2
Tensile Stress (Yield)	245	--	MPa	ISO 527-2
Tensile Strain (Break)	2.4	--	%	ISO 527-2
Flexural Modulus	15000	--	MPa	ISO 178
Flexural Stress	350	--	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Notched Izod Impact	14	--	kJ/m²	ISO 180/A
Unnotched Izod Impact Strength	90	--	kJ/m²	ISO 180

Thermal	Dry	Conditioned	Unit	Test Method
Melting Temperature	260	--	°C	ISO 11357-3

Flammability	Dry	Conditioned		Test Method
Flame Rating (0.800 mm)	HB	--		UL 94

Additional Information
干燥 Typical values shown tested on Dry as Molded samples. Standard Packaging and Labeling: Omnix® 4050 resin is packaged in foil lined, multiwall paper bags containing 25 kg (55 pounds) of material. Individual packages will be plainly marked with the product number, the color, the lot number, and the net weight.

Injection	Dry	Unit
Drying Temperature	80.0	°C
Drying Time	4.0 - 12	hr
Rear Temperature	250	°C
Front Temperature	285	°C
Processing (Melt) Temp	275 - 290	°C
Mold Temperature	80.0 - 120	°C

Injection instructions
Drying: Omnix® 4050 resin is shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Omnix® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Omnix® processing guide. It should be dried before molding because excessive moisture content will result in reduced mechanical properties and processing issues, such as excessive nozzle drooling, foaming and splay visible on the molded parts. Recommended drying conditions are as follows: Type of drier: Desiccant Temperature: 80°C (175°F) Time: 4-12 hours Dew point: -30°C (-22°F) or lower Polyamides oxidize in the presence of oxygen at high temperatures. Therefore drying temperatures above 80°C should be avoided, particularly for light colors or color-controlled parts. Injection Molding: Omnix® 4050 resin can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure. The melt temperature should be between 275°C and 290°C (527°F and 554°F). Generally this can be achieved with barrel temperatures from 250°C (482°F) in the rear zone gradually increasing to 285°C (545°F) in the front zone. Mold temperature should be between 80° and 120°C (176° and 248°F). Set injection pressure to give rapid injection. Adjust holding pressure to one-half injection pressure. Set hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled. Storage: Omnix® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Omnix® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Omnix® processing guide.

Injection instructions

Drying: Omnix® 4050 resin is shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Omnix® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Omnix® processing guide. It should be dried before molding because excessive moisture content will result in reduced mechanical properties and processing issues, such as excessive nozzle drooling, foaming and splay visible on the molded parts. Recommended drying conditions are as follows: Type of drier: Desiccant Temperature: 80°C (175°F) Time: 4-12 hours Dew point: -30°C (-22°F) or lower Polyamides oxidize in the presence of oxygen at high temperatures. Therefore drying temperatures above 80°C should be avoided, particularly for light colors or color-controlled parts. Injection Molding: Omnix® 4050 resin can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure. The melt temperature should be between 275°C and 290°C (527°F and 554°F). Generally this can be achieved with barrel temperatures from 250°C (482°F) in the rear zone gradually increasing to 285°C (545°F) in the front zone. Mold temperature should be between 80° and 120°C (176° and 248°F). Set injection pressure to give rapid injection. Adjust holding pressure to one-half injection pressure. Set hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled. Storage: Omnix® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Omnix® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Omnix® processing guide.

Note Message
1 .	Solvay Test Method. Shrink rates can vary with part design and processing conditions. Please consult a Solvay Technical Representative for more information.

Category:	HPPA , High Performance Polyamide
Manufacturer:	Solvay Specialty Polymers
Trademark:	Omnix®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	TkDxZw_Omnix-4050.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Sylvin 8280-75 Natural	Sylvin Technologies Incorporated	PVC, Flexible	Sylvin
YUNTIANHUA® SF-5	YunNan YunTianHua Co., Ltd.	Acetal (POM) Copolymer	YUNTIANHUA®
Unichem 8711A-02	Colorite Polymers	PVC, Unspecified	Unichem
Amilan® CM3511G33	Toray Resin Company	Nylon Copolymer	Amilan®
ExTima™ GP MB PET 220	Ovation Polymers Inc.	PET	ExTima™