LUVOCOM® 55-9000/WT Datasheet,PC+ABS,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®55-9000/WT is a polycarbonate acrylonitrile butadiene styrene (PC ABS) material,. This product is available in Europe,. LUVOCOM®The main features of 55-9000/WT are: Conductivity Good stiffness Impact resistance Typical application areas include: Electrical/electronic applications Reflector engineering/industrial accessories business/office supplies Sporting goods

General Information
Features	Heat conduction Rigid, good Impact resistance, good Good strength
Uses	Reflector Engineering accessories Switch Business equipment Sporting goods Medical/nursing supplies
Appearance	White

Physical	Nominal Value	Unit	Test Method
Density	1.30	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (260°C/5.0 kg)	< 10.0	cm³/10min	ISO 1133
Molding Shrinkage	0.40 - 0.70	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.20	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	5000	MPa	ISO 527-2
Tensile Stress (Break)	68.0	MPa	ISO 527-2
Tensile Strain (Yield)	3.5	%	ISO 527-2
Flexural Modulus	4500	MPa	ISO 178
Flexural Stress	100	MPa	ISO 178
Flexural Strain at Flexural Strength	5.0	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	140	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+14	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength
-30°C	55	kJ/m²	ISO 179/1fU
23°C	60	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	105	°C	ISO 75-2/A
Continuous Use Temperature	90.0	°C	UL 746B
Vicat Softening Temperature	115	°C	ISO 306/A
CLTE - Flow	6.0E-5	cm/cm/°C	DIN 53752
Thermal Conductivity ¹	1.3	W/m/K

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+14	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature	70.0 - 100	°C
Drying Time	3.0 - 5.0	hr
Suggested Max Moisture	0.020	%
Rear Temperature	210 - 250	°C
Middle Temperature	220 - 260	°C
Front Temperature	230 - 270	°C
Nozzle Temperature	240 - 280	°C
Processing (Melt) Temp	270	°C
Mold Temperature	50.0 - 100	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.02%, otherwise molecular degradation may occur. Suitable heat treatment may increase resistance to the formation of stress cracks. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.02%, otherwise molecular degradation may occur. Suitable heat treatment may increase resistance to the formation of stress cracks. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Note Message
1 .	Hot-Disk, 60x60x3 mm

Category:	PC+ABS , Polycarbonate + ABS
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Tk6yVk_LUVOCOM-55-9000-WT.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
POLYNIL® B40	Nilit Plastics	Nylon 66	POLYNIL®
Sumiflex® K K768DB6	Mitsubishi Chemical Corporation	PVC Elastomer	Sumiflex® K
UBE Polyethylene R300	UBE America, Inc.	PE, Unspecified	UBE Polyethylene
ChronoPrene™ 5A	AdvanSource Biomaterials Corp.	TPE	ChronoPrene™
HiFill® HDPE GF60	Techmer Engineered Solutions	HDPE	HiFill®