Resinoid 2002-4A
| Category: | Phenolic , Phenolic |
| Manufacturer: | Resinoid Engineering Corporation |
| Trademark: | Resinoid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Tiuegv_Resinoid-2002-4A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Resinoid 2002-4A is a fabric reinforced, two-step phenolic molding compound. It has been modified to meet gear requirements and other stressed applications. It possesses excellent impact and flexural strength. It is available in bulk form and is recommended for compression or transfer molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792A, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.20 - 0.40 | % | ASTM D955 |
| Flow direction | 0.20 - 0.40 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr | 0.60 | % | ASTM D570 |
| 23°C, 24 hr | 0.60 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 55.2 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2 |
| Flexural Modulus | |||
| -- | 11000 | MPa | ASTM D790 |
| -- | 75.8 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 96.5 | MPa | ASTM D790 |
| -- | 97.0 | MPa | ISO 178 |
| Compressive Strength | 150 | MPa | ASTM D695, ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -- | 110 | J/m | ASTM D256A |
| -- | 11 | kJ/m² | ISO 180/2A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 177 | °C | ASTM D648, ISO 75-2/A |
| CLTE - Flow | 1.8E-5 | cm/cm/°C | ASTM D696, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 13 | kV/mm | ASTM D149, IEC 60243-1 |
| Additional Information |
|---|
| Molding Pressure - Compression : 2000 to 4000 psi ( 14 to 28 MPa)Molding Temperature, ASTM D957: 300° to 350°F (150° to 175°C) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Staramide BG6ST01 | Eurostar Engineering Plastics | Nylon 6 | Staramide |
| Thermoset Plastics 100 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| EPIMIX POM GFR 25 NC | EPSAN Plastik SAN. ve TiC. A.S. | Acetal (POM) Copolymer | EPIMIX |
| Hanwha Total PP BI961 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |
| LNP™ STAT-KON™ DE004 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |