EPO-TEK® OE100-T
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TiuU2k_EPO-TEK-OE100-T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A two component, high Tg, high temperature grade epoxy designed for semiconductor, underfill, hard-disk drive and hybrid micro-electronics packaging applications. The epoxy can also be used for adhesive and sealing applications in electronics, optical, and medical devices. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Particle Size | < 10.0 | µm |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 468 | °C | |
| Die Shear Strength - >10 kg (23°C) | 23.4 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 250 | °C | |
| Intermittent | -55 to 350 | °C | |
| Storage Modulus (23°C) | 1.68 | GPa | |
| Thixotropic Index | 2.90 | ||
| Weight Loss on Heating | |||
| 200°C | 0.38 | % | |
| 250°C | 0.50 | % | |
| 300°C | 0.84 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 100 | °C | |
| CLTE - Flow | |||
| -- 2 | 4.3E-5 | cm/cm/°C | |
| -- 3 | 1.7E-4 | cm/cm/°C |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Refractive Index 4 | 1.566 | ||
| Transmittance | |||
| 800 nm | 88.0 | % | |
| 880 to 1600 nm | > 94.0 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 10 | ||
| Part B | Mix Ratio by Weight: 1.0 | ||
| Shelf Life (23°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 5 | Amber | ||
| -- 6 | White | ||
| Density | |||
| Part B | 1.02 | g/cm³ | |
| Part A | 1.12 | g/cm³ | |
| Viscosity 7(23°C) | 4.5 to 7.0 | Pa·s | |
| Curing Time (150°C) | 1.0 | hr | |
| Pot Life | 180 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore D) | 87 | ||
| Lap Shear Strength (23°C) | > 13.8 | MPa | |
| Relative Permittivity (1 kHz) | 3.08 | ||
| Volume Resistivity (23°C) | > 1.0E+13 | ohms·cm | |
| Dissipation Factor (1 kHz) | 3.0E-3 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | 589 nm |
| 5 . | Part B |
| 6 . | Part A |
| 7 . | 50 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Provista™ Copolymer ST | Eastman Chemical Company | Polyester, TP | Provista™ |
| Tecnoflon® FOR 5361 | Solvay Specialty Polymers | Fluorelastomer | Tecnoflon® |
| Fainplast PVC RK 330 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| LNP™ THERMOCOMP™ EX06430H compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |
| Sylvin 3260-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |