PALBLEND® R 65
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | pal plast GmbH |
| Trademark: | PALBLEND® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TiYTA3_PALBLEND-R-65.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PALBLEND®R 65 is a polycarbonate acrylonitrile butadiene styrene (PC ABS) product,. It is available in Europe. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 25.0 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.60 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.18 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2100 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield, 23°C) | 47.5 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield, 23°C) | 3.5 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break (23°C) | 50 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 33 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 117 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 300 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information |
|---|
| Melt-Volume Flow Rate, ISO 1133, 260°C/5 kg: 20 to 30 cm³/10 minTensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 2000 to 2200 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 45 to 50 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 3 to 4 %Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: >50 %Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 30 to 35 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 115 to 118 °CDensity, ISO 1183: 1.11 to 1.13 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.5 to 0.7 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.15 to 0.2 % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ENVIROPLAS® ENV08-NC770 | ENVIROPLAS®, Inc. | PBT | ENVIROPLAS® |
| Latamid 66 H2 K/20 | LATI S.p.A. | Nylon 66 | Latamid |
| OnForce™ LFT PP-40LGF/001 Natural | PolyOne Corporation | PP Homopolymer | OnForce™ LFT |
| POLYCOMPO PP E7400 | POLYCOMPO Co.,Ltd. | PP, Unspecified | POLYCOMPO PP |
| Sylvin 8960-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |