Epocast 35-A/927
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Huntsman Advanced Materials |
| Trademark: | Epocast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ti3eer_Epocast-35-A-927.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DESCRIPTION : Epocast® 35-A resin/Hardener 927 epoxy laminating system is a two-component, solvent-free material designed to perform at temperatures up to 300°F (149°C). The medium-viscosity liquid laminating system readily wets glass fabrics; its long work life supports extended fabrication times for large composite repairs. Epocast® 35-A resin/Hardener 927 epoxy laminating system is well suited for repair or fabrication of laminated composite structures and other applications requiring good high-temperatures properties. Epocast® 35-A resin/Hardener 927 epoxy laminating system is qualified to BMS 8-214. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- 1 | 1.00 | g/cm³ | |
| -- | 1.13 | g/cm³ | |
| -- 2 | 1.19 | g/cm³ |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 93 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | ASTM D790 | ||
| 25°C 3 | 19100 | MPa | |
| 25°C 4 | 24000 | MPa | |
| 25°C 5 | 20800 | MPa | |
| 25°C 6 | 26200 | MPa | |
| Flexural Strength | ASTM D790 | ||
| 25°C 7 | 359 | MPa | |
| 25°C 8 | 473 | MPa | |
| 25°C 9 | 534 | MPa | |
| 25°C 10 | 717 | MPa | |
| Compressive Modulus | ASTM D695 | ||
| -- 11 | 6460 | MPa | |
| -- 12 | 9380 | MPa | |
| -- 13 | 25900 | MPa | |
| -- 14 | 27800 | MPa | |
| Compressive Strength | ASTM D695 | ||
| 149°C 15 | 13.8 | MPa | |
| 149°C 16 | 23.4 | MPa | |
| 25°C 17 | 423 | MPa | |
| 25°C 18 | 496 | MPa |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 25 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Thermoset Mix Viscosity | ASTM D2196 | ||
| 25°C 19 | 3200 | cP | |
| 25°C 20 | 25000 | cP | |
| 25°C | 7000 | cP | |
| Demold Time (83°C) | 240 | min | |
| Post Cure Time (121°C) | 2.0 | hr |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Work Life - 100 gms (25°C) | 4.00 to 5.00 | ASTM D1338 |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Resin |
| 3 . | Cure #1, After two hours boiling water |
| 4 . | Cure #2, After two hours boiling water |
| 5 . | Cure #1 |
| 6 . | Cure #2 |
| 7 . | Cure #1, After two hours boiling water |
| 8 . | Cure #2, After two hours boiling water |
| 9 . | Cure #1 |
| 10 . | Cure #2 |
| 11 . | Cure #1, 149°C |
| 12 . | Cure #2, 149°C |
| 13 . | Cure #1, 25°C |
| 14 . | Cure #2, 25°C |
| 15 . | Cure #1, tested at 149°C |
| 16 . | Cure #2, tested at 149°C |
| 17 . | Cure #1 |
| 18 . | Cure #2 |
| 19 . | Resin |
| 20 . | Hardener |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rigidex® P CAP906S | INEOS Olefins & Polymers Europe | PP Impact Copolymer | Rigidex® P |
| Shin-Etsu Elastomer FE-221U | Shin-Etsu Silicones of America | Fluoro Si | Shin-Etsu Elastomer |
| Staramide AG7K | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| Hyundai EP PA66 LD240 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| Kinta NI6000 | Kinta Technology (Hong Kong) Co., Ltd. | Nylon 6 | Kinta |