Moplen HP525J
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | PolyMirae |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ThZgs7_MoplenHP525J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Moplen HP525J is a polypropylene homopolymer designed for the production of biaxially oriented polypropylene films (BOPP). The product is suitable for metallizable film, both as monolayer and in coextruded structures. It contains a standard processing stabilisation but does not contain any slip, antiblocking agents and it is Calcium Stearate free. Moplen HP525J offers good optical, easy processing and very good film profile. Typical applications are BOPP packaging films and Solid Phase Thermoforming sheets. For regulatory information please refer to Moplen HP525J Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 70 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 34.0 | MPa | ISO 527-2/50 |
| Fracture | 23.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 12 | % | ISO 527-2/50 |
| Fracture | > 500 | % | ISO 527-2/50 |
| Flexural Modulus | 1450 | MPa | ISO 178 |
| Coefficient of Friction 1(Dynamic) | 0.50 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Tangent (20 µm) | 3000 | MPa | Internal method |
| Tensile Stress (Break, 20 µm) | 260 | MPa | ISO 527-3/50 |
| Tensile Elongation (Break, 20 µm) | 85 | % | ISO 527-3/50 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 85.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 154 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 2(45°) | 91 | Internal method | |
| Haze 3(50.0 µm) | 0.40 | % | Internal method |
| Additional Information |
|---|
| Film Properties are from monolayer film produced on T.M. Long equipment, a laboratory simultaneous film stretcher (7x7@150°C) |
| Note Message | |
|---|---|
| 1 . | MTM17029E |
| 2 . | MA 17021 |
| 3 . | MA 17031 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE M80064 Series | SABIC Americas, Inc. | HDPE | SABIC® HDPE |
| Spartech Polycom PP5150 | Spartech Polycom | PP Homopolymer | Spartech |
| 4MID® 9AB22240 UV | 4Plas | Nylon 66/6 | 4MID® |
| FHR EPS R-MER II® 5627 (1.25 lb/ft³) | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| Hostaform® C 9021 TF5 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |